Quote:
Originally Posted by nissanfreak317
Dude, I've talked to several seasoned, professional welders, and none of them would go near cast iron, it has a different chemical composition than steel.
Also, It doesn't matter if it's structural or not, if the weld cracks you're leaking exhaust all over the place.
I was just trying to find out what process is being used for this so that I can decide whether or not to give it a try.
|
cool story....I've actually welded cast iron a lot, not talked about it....the weld will not break if the welder is good, in Cody's case, he has a great welder, so it will be fine. Cast aluminum is a bitch to weld, maybe you're thinking of that.....